Concrete Admixtures

---

•  High-range water reducers for low water/cement ratios. Used in SCC and precast. 
•  Water reduction up to 25%
  Compliant with ASTM C494 Type F & G.

•   Speed up setting times, enabling faster finishing and form removal in cold climates. 
•   Reduces set time by 30–60% Non-chloride versions for reinforced concrete.

•  Introduce 4–7% micro air bubbles to increase freeze-thaw resistance.
• ASTM C260 compliant
  Improves durability factor by up to 50%.

•    Delay setting to avoid cold joints or premature stiffening. Useful in hot climates. 
•    Set time extended by 1–3 hours 

•  Prevent segregation in SCC; control slump flow and cohesiveness.
• Recommended for slump flows >650 mm.

•  Lower internal tension from drying shrinkage, reducing surface cracking.
• Shrinkage reduced by up to 30% over 28 days.

For more information on all our solutions:

- write us on: tariq@ingreda.com

• Two-part high-strength bonding system for concrete and steel.
• Tensile strength > 30 MPa
• ASTM C881 compliant

• Seamless, chemical-resistant surfaces for industrial & commercial use.
• Shore D hardness: >75
• Compressive strength: >60 MPa

• Low-viscosity epoxy for crack injection in foundations or columns.
• Viscosity: 200–800 cps
• Crack width: 0.2 mm and above

• Suitable for applications up to 150–180°C. Used in refineries and chemical plants.
• Heat distortion temp: >120°C

• Cure time under 1 hour at 25°C for emergency repairs.
• Initial cure in 30–45 mins

For more information on all our solutions:

- write us on: tariq@ingreda.co

• Applied in a single or two-component format; seamless and UV-resistant.
• Elongation > 300%
• Crack-bridging >1.5 mm

• Pre-formed HDPE/PVC membranes for large-scale roofing and substructures.
• Thickness: 1.2–2 mm
• Water permeability: <1×10⁻¹⁰ cm/s

• Mix-on-site powder applied to concrete surfaces for tanking and substructure.
• Water penetration depth:
  <10 mm (EN 12390-8)

• Penetrates up to 30 mm into concrete and reacts with water to form insoluble crystals.
• Self-healing cracks ≤ 0.4 mm

• Silane/Siloxane-based for surface protection of facades and porous materials.
• VOC-compliant formulas

For more information on all our solutions:

- write us on: tariq@ingreda.com

• Flexible joint sealant with excellent adhesion and movement capacity.
• Movement capability: ±25%
• Shore A: 25–35

• Long-life UV- and weather-resistant sealants for exterior joints.
• UV resistance: 5,000+ hours QUV
• Elongation at break: >400%

• Hard, rigid filler for warehouse floors and airport runways.
• Compressive strength: >70 MPa
• Low shrinkage <0.1%

• Hot- or cold-applied asphaltic sealants for pavements.
• Softening point: 90–110°C
• Flow resistance: >5 mm @ 60°C

• Cost-effective, paintable solutions for indoor expansion joints.
• Elongation at break: 100–150%
• Paintable after 1 hour

For more information on all our solutions:

- write us on: tariq@ingreda.com

• Surface-applied or admixed; migrate to rebar and form a protective film.
• Penetration depth: 10–20 mm
• Chloride-induced corrosion reduction: ≥70%

• Applied post-construction to extend the service life of RC structures.
• Effective for >5 years of exposure

• Mixed directly into concrete to provide passive protection.
• Dosage: 1.5–3.0 L/m³
• pH compatible, non-toxic

• Zinc-based embedded anodes prevent localized corrosion at repairs.
• Service life: 10–15 years
• Output: 1.0–2.0 mA per anode

• Neutralize existing rust and convert to a stable black magnetite layer.
• Reaction time: 30–60 mins
• VOC: <50 g/L

For more information on all our solutions:

- write us on: tariq@ingreda.com